Synthesis and luminescent properties of gadolinium tantalum niobates Gd(Nb$_{0.9}$Ta$_{0.1})$O$_{4}$
E. V. Ivanovaa, S. M. Masloboevab, V. A. Kraveza, K. N. Orekhovaa, G. A. Guseva, A. N. Trofimova, O. B. Shcherbinab, M. A. Yagovkinaa, A. A. Averinc, M. V. Zamoryanskayaa a Ioffe Institute, St. Petersburg, Russia
b Tananaev Institute of Chemistry – Subdivision of the Federal Research Centre "Kola Science Centre of the Russian Academy of Sciences" Science Centre of Russian Academy of Sciences,
Apatity, Murmansk region, Russia
c Frumkin Institute of Physical chemistry and Electrochemistry Russian academy of sciences, Moscow, Russia
Аннотация:
The feasibility of synthesizing gadolinium tantalum niobates by the liquid-phase method was demonstrated. The methods of X-ray diffraction, electron probe microanalysis, local cathodoluminescence, and photoluminescence were applied to study the samples. It was shown that under the selected synthesis conditions ($T\sim$ 1400$^\circ$C for 3 hours), no solid solution of niobium-tantalum was formed in the powder samples. When obtaining ceramic samples, it was possible to obtain a solid solution and to study the dependence of the luminescence intensity on the niobium content upon excitation of the samples by an electron beam. The maximum luminescence intensity was observed in the sample with the composition of GdNb$_{0.9}$Ta$_{0.1}$O$_{4}$. It was shown that the inhomogeneity of luminescence is not related to fluctuations in composition, but is related to the inhomogeneous distribution of vacancy centers, which are luminescence centers.
Ключевые слова:
gadolinium tantalum niobates, cathodoluminescence, X-ray diffraction, electron probe microanalysis, liquid-phase synthesis.
Поступила в редакцию: 01.10.2019 Исправленный вариант: 01.10.2019 Принята в печать: 05.11.2019
Образец цитирования:
E. V. Ivanova, S. M. Masloboeva, V. A. Kravez, K. N. Orekhova, G. A. Gusev, A. N. Trofimov, O. B. Shcherbina, M. A. Yagovkina, A. A. Averin, M. V. Zamoryanskaya, “Synthesis and luminescent properties of gadolinium tantalum niobates Gd(Nb$_{0.9}$Ta$_{0.1})$O$_{4}$”, Оптика и спектроскопия, 128:2 (2020), 228; Optics and Spectroscopy, 127:6 (2019), 1011–1017
Образцы ссылок на эту страницу:
https://www.mathnet.ru/rus/os471 https://www.mathnet.ru/rus/os/v128/i2/p228
|
Статистика просмотров: |
Страница аннотации: | 26 | PDF полного текста: | 12 |
|