Synthesis and comparative photocatalytic activity of CuO layers on SiO$_{2}$ substrates
E. V. Polyakov, R. R. Tzukanov, I. V. Volkov, L. Yu. Buldakova, I. V. Baklanova, O. A. Lipina, V. P. Zhukov, Yu. V. Kuznetsova, A. P. Tutyunnik, M. A. Maximova Institute of Solid State Chemistry UB RAS, 91, Pervomaiskaya str.,
Ekaterinburg, 620990, Russian Federation
Аннотация:
Using the thermodynamic and kinetic approaches, it was found that Cu(NH$_{3}$)$^{2+}_{4 aq}$ complex predominating at 23$^{\circ}$C spontaneously decomposes at elevated temperatures, forming CuO precipitate in a bulk solution and a layer (CuO||SiO$_{2}$) on the surface of silica glass. The rates of these heterogeneous processes are fairly well described by the 1st-order reaction of decay of the Cu(NH$_{3}$)$^{2+}_{4 aq}$ complex. The formation of the CuO precipitate and layer is a two-step kinetic process. The rate of precipitate formation dominates above 65$^{\circ}$C while the rate of the layer formation prevails below this value. The CuO$\parallel$SiO$_{2}$ material synthesized below 65 possesses an optical bandgap of (1.25 0.05) eV, which is smaller compared to the crystals of commercial CuO. The CuO||SiO$_{2}$ material displays a photocatalytic activity in the reaction of UV-decomposition of benzoquinone-hydroquinone. It was discovered that the photocatalytic activity depends on the thickness of the photocatalyst layer.
Ключевые слова:
Copper(II), oxide, layer, glass, surface, kinetics, photocatalyst.
Поступила в редакцию: 18.09.2020
Образец цитирования:
E. V. Polyakov, R. R. Tzukanov, I. V. Volkov, L. Yu. Buldakova, I. V. Baklanova, O. A. Lipina, V. P. Zhukov, Yu. V. Kuznetsova, A. P. Tutyunnik, M. A. Maximova, “Synthesis and comparative photocatalytic activity of CuO layers on SiO$_{2}$ substrates”, Наносистемы: физика, химия, математика, 11:5 (2020), 601–607
Образцы ссылок на эту страницу:
https://www.mathnet.ru/rus/nano563 https://www.mathnet.ru/rus/nano/v11/i5/p601
|
Статистика просмотров: |
Страница аннотации: | 41 | PDF полного текста: | 41 |
|