Temperature influence study on copper selenide films
V. Rajendrana, S. Arulmozhi Packiaseelib, S. Muthumaric, R. Vijayalakshmic a Department of Physics, Vivekananda College, Madurai 625234, India
b P. G. and Research Department of Physics, Fatima College, Madurai 625018, India
c P. G. and Research Department of Physics, Thiagarajar College, Madurai 625009, India
Аннотация:
Copper selenide was prepared by film is successfully deposited on a Fluorine-doped Tin Oxide (FTO) substrate by a brush plating technique. The film was uniform, had good adherence to the substrate and was annealed at 300$^\circ$ C and 500$^\circ$C. As the annealing temperature increased, the orientation of the crystallites is more randomized than in the as-prepared film. The structural and optical properties of the film were investigated by XRD, SEM, EDAX, UV-Visible and PL. The XRD pattern indicated that this film was crystalline in the structure.
Ключевые слова:
Brush plating, copper selenide, optical properties.
Поступила в редакцию: 05.02.2016 Исправленный вариант: 03.05.2016
Образец цитирования:
V. Rajendran, S. Arulmozhi Packiaseeli, S. Muthumari, R. Vijayalakshmi, “Temperature influence study on copper selenide films”, Наносистемы: физика, химия, математика, 7:4 (2016), 699–702
Образцы ссылок на эту страницу:
https://www.mathnet.ru/rus/nano269 https://www.mathnet.ru/rus/nano/v7/i4/p699
|
Статистика просмотров: |
Страница аннотации: | 60 | PDF полного текста: | 33 |
|