The characterization of nanosized $\mathrm{ZnFe}_2\mathrm{O}_4$ material prepared by coprecipitation
A. T. Nguyena, Ph. H. Nh. Phana, I. Ya. Mittovab, M. V. Knurovab, V. O. Mittovac a Ho Chi Minh City Pedagogical University, Ho Chi Minh City, Vietnam
b Voronezh State University, Voronezh, Russia
c Voronezh State Medical University named after N.N. Burdenko, Voronezh, Russia
Аннотация:
The nanosized $\mathrm{ZnFe}_2\mathrm{O}_4$ material was synthesized using the coprecipitation method from $\mathrm{Zn}^{2+}$ and $\mathrm{Fe}^{3+}$ cations in a boiling aqueous medium. The results of TG/DSC, XRD, SEM, TEM and VSM analysis show that the $\mathrm{ZnFe}_2\mathrm{O}_4$ material prepared after annealing at $600^\circ$C had tetragonal structure, a size of $20$ – $50$ nm, $H_c<70$ Oe, $M_r<0.5$ emu/g and $M_s\sim2.5$ emu/g.
Ключевые слова:
sol-gel synthesis, nanopowders, zinc ferrite, magnetic properties.
Поступила в редакцию: 18.01.2016
Образец цитирования:
A. T. Nguyen, Ph. H. Nh. Phan, I. Ya. Mittova, M. V. Knurova, V. O. Mittova, “The characterization of nanosized $\mathrm{ZnFe}_2\mathrm{O}_4$ material prepared by coprecipitation”, Наносистемы: физика, химия, математика, 7:3 (2016), 459–463
Образцы ссылок на эту страницу:
https://www.mathnet.ru/rus/nano219 https://www.mathnet.ru/rus/nano/v7/i3/p459
|
Статистика просмотров: |
Страница аннотации: | 74 | PDF полного текста: | 58 |
|