Chemical composition of surface and structure of defects in diamond single crystals produced from detonation nanodiamonds
S. V. Kidalova, V. V. Shnitova, M. V. Baidakovaa, M. M. Brzhezinskayab, A. T. Dideikina, M. S. Shestakova, D. A. Smirnovb, I. T. Serenkova, V. I. Sakharova, V. V. Sokolova, N. I. Tatarnikova, A. Ya. Vul'a a Ioffe Institute, Polytechnicheskaya 26, St. Petersburg, 194021, Russia
b Helmholtz Zentrum Berlin Mat & Energie, D-12489 Berlin, Germany
Аннотация:
We present the results from our investigation of the structure and composition of microcrystalline diamonds obtained by sintering at high pressures and at high temperatures of detonation nanodiamond particles. Using XPS, XAS and photoluminescence spectroscopy, we found that the surface’s chemical composition and a defects structure of microcrystalline diamonds significantly differ from the initial detonation nanodiamonds. This indicates the essential transformation of structure and composition of initial detonation nanodiamonds particles during the formation of single crystals at high pressure and temperature.
Ключевые слова:
detonation nanodiamond, HPHT sintering, single crystal, XPS and XAS spectroscopy, photoluminescence, defects.
Поступила в редакцию: 20.06.2017 Исправленный вариант: 27.09.2017
Образец цитирования:
S. V. Kidalov, V. V. Shnitov, M. V. Baidakova, M. M. Brzhezinskaya, A. T. Dideikin, M. S. Shestakov, D. A. Smirnov, I. T. Serenkov, V. I. Sakharov, V. V. Sokolov, N. I. Tatarnikov, A. Ya. Vul', “Chemical composition of surface and structure of defects in diamond single crystals produced from detonation nanodiamonds”, Наносистемы: физика, химия, математика, 9:1 (2018), 21–24
Образцы ссылок на эту страницу:
https://www.mathnet.ru/rus/nano114 https://www.mathnet.ru/rus/nano/v9/i1/p21
|
Статистика просмотров: |
Страница аннотации: | 71 | PDF полного текста: | 15 |
|