The electroluminescent devices presented in this paper were fabricated using poly[1,4-phenylene-1,2-di(4-phenoxyphenyl) vinylene] as a light-emitting layer; green emission was observed with maximum wavelength at 530 nm and emission energy 3.8×10−4 J cm−2, achieved at current density 41.6 mA cm−2.
Тип публикации:
Статья
Язык публикации: английский
Образец цитирования:
A. V. Vannikov, A. Ch. Saidov, “Electroluminscence in Ether-substituted Poly(phenylenevinylenes)”, Mendeleev Commun., 3:2 (1993), 54–56
Образцы ссылок на эту страницу:
https://www.mathnet.ru/rus/mendc5263
https://www.mathnet.ru/rus/mendc/v3/i2/p54
Эта публикация цитируется в следующих 4 статьяx:
E. I. Mal'tsev, D. A. Lypenko, A. V. Dmitriev, A. V. Vannikov, A. S. Burlov, V. G. Vlasenko, “Electroluminescence and Organic Light-Emitting Diodes”, Russ J Coord Chem, 49:S1 (2023), S2
Y.-H. Tak, H. Vestweber, H. Bässler, A. Bleyer, R. Stockmann, H.-H. Hörhold, “Time-resolved electroluminescence from single and bilayer LEDs based upon substituted poly-arylenevinylenes”, Chemical Physics, 212:2-3 (1996), 471
E.I. Mal'tsev, M.A. Brusentseva, V.A. Kolesnikov, A.V. Vannikov, “Electroluminescence of poly(hydroxyamino esters)-aluminum complexes”, Chemical Physics Letters, 238:4-6 (1995), 295
H.-H. Hörhold, A. Bleyer, E. Birckner, S. Heinze, F. Leonhardt, “A novel approach to light emitting polyarylenes: Cyclization of poly(arylene vinylenes)”, Synthetic Metals, 69:1-3 (1995), 525
Обратная связь: