Influence of Dislocation Density of Copper Electrode on the Kinetics of Anode Process in Acidic $\rm CuSO_4$ Solution

Deformed copper samples were burned at different temperatures. This procedure formed different dislocation density in the samples. Then such prepared samples were used as the anodes in acidic $\mathrm{CuSO}_{4}$ solution. The voltage for electrolyse was $10$ mV. The experiment has shown that the increase of the dislocation density in the anode leads to the increase of the density of anode current. It was discovered that the density of anode current could become $2,5$ times bigger. This can be explained by the fact that dislocations decrease the potential barrier during the transfer of copper ions from the grid into the electrolyte.