Anti-scratch AlMgB$_{14}$ Gorilla$^{\circledR}$ Glass coating
V. V. Putrolaynena, A. M. Grishinabc, I. V. Rigoeva a Petrozavodsk State University
b KTH Royal Institute of Technology, Stockholm-Kista, Sweden
c INMATECH Intelligent Materials Technology, Skärholmen, Sweden
Abstract:
Hard aluminum–magnesium boride (BAM) films were fabricated onto Corning$^{\circledR}$ Gorilla$^{\circledR}$ Glass by radio-frequency magnetron sputtering of a single stoichiometric AlMgB$_{14}$ target. BAM films exhibit a Vickers hardness from 10 to 30 GPa and a Young’s modulus from 80 to 160 GPa depending on applied loading forces. Deposited hard coating increases the critical load at which glass substrate cracks. The adhesion energy of BAM films on Gorilla$^{\circledR}$ Glass is 6.4 J/m$^2$.
Received: 20.03.2017
Citation:
V. V. Putrolaynen, A. M. Grishin, I. V. Rigoev, “Anti-scratch AlMgB$_{14}$ Gorilla$^{\circledR}$ Glass coating”, Pisma v Zhurnal Tekhnicheskoi Fiziki, 43:19 (2017), 3–11; Tech. Phys. Lett., 43:10 (2017), 871–874
Linking options:
https://www.mathnet.ru/eng/pjtf6102 https://www.mathnet.ru/eng/pjtf/v43/i19/p3
|
Statistics & downloads: |
Abstract page: | 36 | Full-text PDF : | 9 |
|