Optically induced effects in irradiated ultrafine Al$_{2}$O$_{3}$–BeO ceramics
S. V. Nikiforov, A. D. Borbolin, A. Yu. Marfin, A. F. Nikiforov Ural Federal University named after the First President of Russia B. N. Yeltsin, Ekaterinburg
Abstract:
We studied optically induced effects in ultrafine Al$_{2}$O$_{3}$–BeO ceramics irradiated with a high-dose pulsed electron beam (130 keV). Upon optical excitation of ceramics at 470 nm, optically stimulated luminescence is observed due to the depletion of traps associated with thermoluminescence peaks at 380 and 530 K. These traps are characterized by a complex energy spectrum with a nonuniformly distributed photoionization cross section. The prospects of using optically stimulated luminescence of Al$_{2}$O$_{3}$–BeO ceramics in high-dose dosimetry (3–30 kGy) have been proved.
Keywords:
themoluminescence, optically stimulated luminescence, high-dose dosimetry, ultrafine ceramics, photoionization cross section.
Received: 22.04.2019 Revised: 22.04.2019 Accepted: 09.07.2019
Citation:
S. V. Nikiforov, A. D. Borbolin, A. Yu. Marfin, A. F. Nikiforov, “Optically induced effects in irradiated ultrafine Al$_{2}$O$_{3}$–BeO ceramics”, Pisma v Zhurnal Tekhnicheskoi Fiziki, 45:21 (2019), 15–18; Tech. Phys. Lett., 45:11 (2019), 1078–1081
Linking options:
https://www.mathnet.ru/eng/pjtf5274 https://www.mathnet.ru/eng/pjtf/v45/i21/p15
|
Statistics & downloads: |
Abstract page: | 37 | Full-text PDF : | 8 |
|