Studying the grain structure of SMS targets manufactured under variable conditions
I. S. Volchkov, E. B. Baskakov, V. I. Strelov, V. M. Kanevskii FSRC "Crystallography and Photonics" RAS
Abstract:
The grain structure of samarium sulfide (SmS) targets manufactured by pressing with or without subsequent high-temperature treatment by high-frequency current (HFC) at various pressures has been studied. The density of samples manufactured in various regimes was determined and the optimum technological conditions for obtaining high-quality SMS targets were selected. In particular, the HFC annealing upon pressing at 5 t/cm$^2$ proved to be more effective than the analogous treatment at 4 t/cm$^2$. It is established that the samples obtained by pressing at 5 t/cm$^2$ without high-temperature HFC annealing contain significant amounts of unbound metallic samarium.
Keywords:
samarium sulfide, grain structure, scanning electron microscopy.
Received: 29.04.2019 Revised: 29.04.2019 Accepted: 23.07.2019
Citation:
I. S. Volchkov, E. B. Baskakov, V. I. Strelov, V. M. Kanevskii, “Studying the grain structure of SMS targets manufactured under variable conditions”, Pisma v Zhurnal Tekhnicheskoi Fiziki, 45:22 (2019), 12–15; Tech. Phys. Lett., 45:11 (2019), 1127–1130
Linking options:
https://www.mathnet.ru/eng/pjtf5260 https://www.mathnet.ru/eng/pjtf/v45/i22/p12
|
Statistics & downloads: |
Abstract page: | 49 | Full-text PDF : | 30 |
|