Morphology, structural and optical properties of silicon nanostructures obtained in a solution containing hexafluorosilicic acid H$_{2}$(SiF$_{6}$)
Sh. A. Zhumatova, S. M. Manakov, Y. Sagidolda, M. B. Darmenkulova, R. M. Azamat, B. E. Alpysbayeva, K. K. Dikhanbayev Al-Farabi Kazakh National University
Abstract:
Boron doped porous silicon with the observed photoluminescence with a crystallographic orientation of (100), which was fabricated based on a $p$-type silicon substrate using electrochemical etching in a solution containing hexafluorosilicic acid and ethyl alcohol was studied. A comparative analysis of the morphology, structural and optical properties of silicon nanostructures obtained in a solution containing H$_{2}$(SiF$_{6}$) and ethanol and samples obtained in a solution containing HF and ethanol was performed. Morphology, structural and optical properties were studied using scanning probe microscopy and spectrophotometry. It was shown that samples of porous silicon obtained in a solution containing H$_{2}$(SiF$_{6}$) and ethanol are characterized by improved optical properties, in particular, they exhibit more intense photoluminescence compared to samples obtained in solutions with HF and ethyl alcohol.
Keywords:
porous silicon, optical properties, electrochemical etching, photoluminescence, reflection index.
Received: 02.05.2020 Revised: 02.05.2020 Accepted: 20.05.2020
Citation:
Sh. A. Zhumatova, S. M. Manakov, Y. Sagidolda, M. B. Darmenkulova, R. M. Azamat, B. E. Alpysbayeva, K. K. Dikhanbayev, “Morphology, structural and optical properties of silicon nanostructures obtained in a solution containing hexafluorosilicic acid H$_{2}$(SiF$_{6}$)”, Optics and Spectroscopy, 128:9 (2020), 1375–1379; Optics and Spectroscopy, 128:9 (2020), 1487–1491
Linking options:
https://www.mathnet.ru/eng/os317 https://www.mathnet.ru/eng/os/v128/i9/p1375
|
Statistics & downloads: |
Abstract page: | 46 | Full-text PDF : | 11 |
|