Elastically strained and relaxed La$_{0.67}$Ca$_{0.33}$MnO$_{3}$ films grown on lanthanum aluminate substrates with different orientations
Yu. A. Boikova, I. T. Serenkova, V. I. Sakharova, T. Claesonb a Ioffe Institute, St. Petersburg
b Chalmers University of Technology, Gothenburg, Sweden
Abstract:
Structure of 40-nm thick La$_{0.67}$Ca$_{0.33}$MnO$_{3}$ (LCMO) films grown by laser evaporation on (001) and (110) LaAlO$_3$ (LAO) substrates has been investigated using the methods of medium-energy ion scattering and X-ray diffraction. The grown manganite layers are under lateral biaxial compressive mechanical stresses. When (110)LAO wafers are used as the substrates, stresses relax to a great extent; the relaxation is accompanied by the formation of defects in a (3–4)-nm thick manganite-film interlayer adjacent to the LCMO–(110)LAO interface. When studying the structure of the grown layers, their electro- and magnetotransport parameters have been measured. The electroresistance of the LCMO films grown on the substrates of both types reached a maximum at temperature $T_M$ of about 250 K. At temperatures close to $T_M$ magnetoresistance of the LCMO/(110)LAO films exceeds that of the LCMO/(001)LAO films by 20–30%; however, the situation is inverse at low temperatures ($T<$ 150 K). At $T<T_M$, the magnetotransport in the grown manganite films significantly depends on the spin ordering in ferromagnetic domains, which increase with a decrease in temperature.
Received: 11.05.2016
Citation:
Yu. A. Boikov, I. T. Serenkov, V. I. Sakharov, T. Claeson, “Elastically strained and relaxed La$_{0.67}$Ca$_{0.33}$MnO$_{3}$ films grown on lanthanum aluminate substrates with different orientations”, Fizika Tverdogo Tela, 58:12 (2016), 2469–2475; Phys. Solid State, 58:12 (2016), 2560–2566
Linking options:
https://www.mathnet.ru/eng/ftt9761 https://www.mathnet.ru/eng/ftt/v58/i12/p2469
|
Statistics & downloads: |
Abstract page: | 20 | Full-text PDF : | 6 |
|